Tuairisgeul
Meud àbhaisteach
|
Raon OD (mm) |
Fulangas OD (mm) |
Ovality |
Bogha |
|
OD Nas lugha na no co-ionann ri 5.0 |
±2.00% OD |
2.00% |
0.20% |
|
5.0＜OD＜10.0 |
±1.00% OD |
1.00% |
0.10% |
|
10.0＜OD＜20.0 |
±1.00% OD |
1.00% |
0.10% |
|
20.0＜OD＜30.0 |
±1.00% OD |
1.00% |
0.10% |
|
30.0＜OD＜50.0 |
±1.00% OD |
1.00% |
0.10% |
|
50.0＜OD＜100.0 |
±1.00% OD |
1.00% |
0.15% |
|
100.0＜OD＜160.0 |
±1.00% OD |
1.00% |
0.15% |
Susbaint neo-dhìomhaireachd
|
Còd |
Slatan-tomhais |
Al |
ca |
Cr |
Cu |
Fe |
K |
|
PQ191E |
àbhaisteach |
13.0 |
0.50 |
<0.05 |
<0.05 |
0.10 |
0.10 |
|
As àirde |
19.0 |
1.00 |
0.10 |
0.10 |
0.50 |
1.00 |
|
|
PQ191EH |
àbhaisteach |
8.0 |
0.60 |
<0.05 |
<0.01 |
0.10 |
0.10 |
|
As àirde |
10.0 |
1.00 |
0.10 |
<0.01 |
0.50 |
0.50 |
|
|
Còd |
Slatan-tomhais |
Li |
Tha mg |
Mn |
Na |
Ti |
Zr |
|
PQ191E |
àbhaisteach |
0.3 |
0.05 |
0.05 |
0.10 |
1.30 |
1.00 |
|
As àirde |
1.00 |
0.20 |
0.20 |
1.00 |
2.00 |
2.00 |
|
|
PQ191EH |
àbhaisteach |
0.20 |
0.05 |
0.05 |
0.10 |
1.30 |
1.00 |
|
As àirde |
0.50 |
0.20 |
0.20 |
0.50 |
2.00 |
2.00 |
Feartan
- Sùbailteachd Customization
- Dearbhadh Càileachd - àrd
- Cosgais - Coileanadh Èifeachdach
- Lìbhrigeadh luath agus earbsach
Raointean Iarrtais
- Gnìomhachas petroceimiceach
- Gnìomhachas Cungaidh-leigheis
- Innleadaireachd Àrainneachdail
Feartan
|
Feartan corporra |
Luachan |
|
Purity |
＞99.99% |
|
Dùmhlachd |
2.2g / cm3 |
|
follaiseachd |
＞90% |
|
Mohs cruas |
5.5--6.5 |
|
Rubha deformation |
1280 ceum |
|
Puing lasachaidh |
1750 ceum |
|
Rubha analachaidh |
1250 ceum |
|
Teas sònraichte (20 - 350 ceum ) |
670J/kg. ceum |
|
Giùlan teirmeach (20 ceum) |
1.4W/m. ceum |
|
Giùlan teas (w / mk, 1000 ceum) |
1.0-1.2 |
|
Clàr-innse Refractive |
1.4585 |
|
Coefficient de Thermal Leudachadh |
5.510 -7cm/cm. ceum |
|
Teòthachd obrach - teth |
1750- -2050 ceum |
|
Teòthachd seirbheis goirid - |
1450 ceum |
|
Teòthachd seirbheis fad-ùine - |
1100 ceum |
|
Feartan ceimigeach |
Luachan |
|
A 'seasamh an aghaidh searbhag |
Acid làidir (ach a-mhàin HF), alkali làidir, fuasgladh organach |
|
Teòthachd àrd resistant creimeadh |
Sgoinneil |
|
Susbaint Impurity Meatailt |
＜5 ppm |
|
Feartan dealain |
Luachan |
|
Resistivity |
7107Ω.cm |
|
Neart Insulation |
250 ~ 400Kv / cm |
|
Constant dielectric |
3.7~3.9 |
|
Co-èifeachd in-ghabhail dielectric |
＜410-4 |
|
Co-èifeachd call dielectric |
＜110-4 |
|
Feartan meacanaigeach |
Luachan |
|
Neart teannachaidh |
1100MPa |
|
Neart lùbte |
67 MPa |
|
Neart tensile |
48 MPa |
|
Co-mheas Poisson |
0.14~0.17 |
|
Modulus Young |
72000 mpa |
|
Modulus rùsgaidh |
31000MPa |
Ceistean Cumanta
C: Dè na trast-thomhas agus fulangas a tha rim faighinn?
A: Raon àbhaisteach:
- Trast-thomhas: 1mm–150mm (±0.05mm)
- Faid: suas gu 2000mm (±1mm)
- Meudan gnàthaichte le fulangas nas teinne (±0.01mm)
C: An urrainnear na slatan quartz a innealachadh às deidh an lìbhrigeadh?
A: Tha, tha sinn a 'moladh:
- Inneal daoimean airson gearradh
- CO₂ laser drilling (for holes >0.5mm)
- Snasadh teine airson làimhseachadh oir
C: A bheil na slatan quartz agad freagarrach airson stiùiridhean solais UV?
A: Tha, le:
- >Tar-chuir 90% @ 185nm (ìre UV)
- Uachdaran roghnach air an snìomh (Ra<1nm)
C: Ciamar a tha slatan air am pacadh gus casg a chuir air milleadh?
A: Dìon ioma-fhilleadh:
- Muilnean PVC fa leth
- Foam-cliabhan fiodha air an sgaradh
- Pocannan dìon taise -(glanadh nitrogen roghnach)
Teachdaichean teth: slat quartz, luchd-saothrachaidh slat quartz Sìona, solaraichean, factaraidh
Cuir rannsachadh
Is dòcha gum bu toil leat cuideachd